What wear parts are available for Hazemag HSI Impact Crushers?

Anranst supplies complete wear parts for Hazemag HSI Impact Crushers, including jaw plates, cone liners, blow bars, and other critical wear components. All parts are OEM-compatible and available in multiple material grades (Mn13Cr2, Mn18Cr2, Cr26 high-chrome iron, Cr-Mo alloy steel, WC-Co cemented carbide) to match your specific ore conditions.

What materials does Anranst recommend for Hazemag HSI Impact Crushers wear parts?

Material selection depends on your crushing application: Mn13Cr2 (ASTM A128 B-2) for moderate impact with work-hardening; Mn18Cr2 for harder abrasive feed with 30-50% longer life; Cr26 high-chrome iron for high-abrasion low-impact zones; Cr-Mo alloy steel for SAG mill liners; WC-Co for HPGR studs. Our engineers can recommend the optimal grade based on your ore characteristics.

How long is the delivery time for Hazemag HSI Impact Crushers wear parts?

Standard sizes are available for rapid delivery. Custom orders typically ship within 4-6 weeks. Emergency supply is available for critical operations with 72-hour delivery for in-stock items. Contact our sales team for specific delivery estimates.

Are Anranst wear parts compatible with OEM Hazemag equipment?

Yes. All Anranst wear parts are manufactured to OEM dimensions with guaranteed interchangeability. We use CMM inspection against OEM drawings and provide full metallurgical traceability. No modifications needed for drop-in replacement.

Overview

Technical Specs

Wear Parts

Hazemag

HSI Impact Crushers

Name: HSI Impact Crushers — Hazemag
Brand: Hazemag
Availability: InStock

Hazemag HSI (Horizontal Shaft Impact) crushers are world-renowned for their versatility in primary and secondary crushing. The patented SKR rotor design provides optimal blow bar utilization and rapid changeover. Models from APKV to APKV-MH handle capacities up to 2,500 tph in recycling, mining and aggregate applications. Anranst supplies blow bars in Mn18Cr2 work-hardening steel and Cr26 high-chrome iron for different feed conditions.

Typical Applications

casting High Alloy Wear-resistant Casting wear-resistant casting hammerhead wear-resistant casting epoxy wear-resistant casting rod wear resistant casting Forged Wear Parts forged car parts difference between forged and rotary forged wheels how to make a forged knife hot forged vs cold forged differ

Factory

Production Gallery — Anranst Workshop

Technical Data

HSI Impact Crushers — Models

Models	Wear Parts
Models	HCS/HRC series
Capacity	50-1,500 tph
Max Feed	Up to 1,500mm
Rotor Diameter	Various
Power	90-630 kW

Compatible Models (from OEM catalog)

HCS 0610HCS 0616HCS 0620HCS 0625HCS 0816HCS 0820HCS 0825HCS 0830HCS 1020HCS 1025HCS 1030HCS 1040HCS 1320HCS 1330HCS 1340HCS 0510HCS 0516HCS 0520HCS 0630HCS 0810HCS 0840HRC 0505HRC 0507HRC 0510HRC 0605HRC 0607HRC 0610HRC 0616HRC 0620HRC 0810HRC 0816HRC 0820HRC 1010HRC 1016HRC 1020HRC 1210HRC 1216HRC 1220HRC 1225HRC 1230

Crushing Stage

Primary, Quaternary

Wear Parts

for | | |cement and mining machinery | | |parts | |?????? |Mining Machinery Parts | |??????? |Rock crusher parts | |?????

Wear Parts

HSI Impact Crushers Wear Parts

Models

HCS/HRC series

Wear Parts

Blow bars, Impact plates

Blow Bar / Impact Hammer

High-speed rotating impact element for APP/APK/APK-V series; launches material against impact plates at 30-60 m/s for primary/secondary crushing

Mn13Cr2ASTM A128 Grade B-2 / GB ZGMn13-2

HardnessHB 210-260 (work-hardens to HRC 45-55)

ToughnessAKV ≥ 80J

Tensile Strength≥ 750 MPa

Yield Strength≥ 380 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Mn13Cr2	1.05-1.20	≤1.0	11.5-14.0	1.5-2.5	—	—

Excellent work-hardening capability; surface hardness increases under impact, ideal for moderate to high impact crushing conditions

Cr26ASTM A532 Class III Type A / GB KmTBCr26

HardnessHRC 58-65

ToughnessAKV 5-8J

Tensile Strength≥ 500 MPa

Yield Strength—

Grade	C	Si	Mn	Cr	Mo	Ni
Cr26	2.0-3.3	≤1.0	0.5-1.5	23.0-30.0	1.0-3.0	≤1.5

Excellent abrasion resistance with M7C3 carbide network; 3-5x longer life than Mn steel in pure abrasive wear; ideal for vertical mill rollers and VSI rotors

Cr-Mo Alloy SteelASTM A217 WC6/WC9 / GB ZG15CrMo

HardnessHRC 42-52

ToughnessAKV ≥ 25J

Tensile Strength≥ 750 MPa

Yield Strength≥ 550 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Cr-Mo Alloy Steel	0.15-0.25	0.30-0.60	0.50-0.80	1.00-1.50	0.45-0.65	—

Good combination of hardness and toughness; ideal for SAG mill liners, grate bars and crusher frame liners under abrasive wear

Bimetal Cr26+Carbon SteelBimetal Composite / Cr26 + Low Carbon Steel

HardnessHRC 62+ (wear layer) / HB 180-220 (base)

ToughnessAKV ≥ 50J (base layer)

Tensile Strength≥ 600 MPa (composite)

Yield Strength≥ 350 MPa (base)

Grade	C	Si	Mn	Cr	Mo	Ni
Bimetal Cr26+Carbon Steel	2.0-3.0 / 0.15-0.25	≤1.0 / 0.30-0.60	0.5-1.5 / 0.60-1.00	23.0-30.0 / ≤0.50	1.0-3.0 / —	≤1.0 / —

Dual-layer casting: Cr26 wear surface + ductile steel base; combines extreme abrasion resistance with structural integrity; 1.5-2x longer life than monolithic Cr26 for large hammers

Impact Plate / Anvil

Stationary crushing surface; adjustable gap and angle control product size and shape; hydraulically adjustable in APP series

Mn18Cr2ASTM A128 Grade B-4 / GB ZGMn18Cr2

HardnessHB 230-300 (work-hardens to HRC 48-58)

ToughnessAKV ≥ 60J

Tensile Strength≥ 800 MPa

Yield Strength≥ 420 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Mn18Cr2	1.05-1.35	≤1.0	16.0-19.0	1.5-2.5	—	—

Higher Mn content provides superior work-hardening depth; 20-30% longer service life than Mn13 in high-compression applications

Impact Plate / Apron

Hazemag HSI primary and secondary impact aprons; adjustable gap for product size control

Mn13Cr2ASTM A128 Grade B-2 / GB ZGMn13Cr2

HardnessHB 210-260 (work-hardens to HRC 45-55)

ToughnessAKV ≥ 80J

Tensile Strength≥ 750 MPa

Yield Strength≥ 380 MPa

Grade	C	Si	Mn	Cr
Mn13Cr2	1.05-1.35	≤1.0	11.0-14.0	1.5-2.5

Standard work-hardening steel; cost-effective for moderate impact applications

Mn18Cr2ASTM A128 Grade B-4 / GB ZGMn18Cr2

HardnessHB 230-300 (work-hardens to HRC 48-58)

ToughnessAKV ≥ 60J

Tensile Strength≥ 800 MPa

Yield Strength≥ 420 MPa

Grade	C	Si	Mn	Cr
Mn18Cr2	1.05-1.35	≤1.0	16.0-19.0	1.5-2.5

Superior work-hardening depth; 20-30% longer life than Mn13 in high-compression applications

Liner Plate

Internal housing liner plates protecting Hazemag crusher body from material impact and abrasion

Mn13Cr2ASTM A128 Grade B-2 / GB ZGMn13Cr2

HardnessHB 210-260 (work-hardens to HRC 45-55)

ToughnessAKV ≥ 80J

Tensile Strength≥ 750 MPa

Yield Strength≥ 380 MPa

Grade	C	Si	Mn	Cr
Mn13Cr2	1.05-1.35	≤1.0	11.0-14.0	1.5-2.5

Standard work-hardening steel; cost-effective for moderate impact applications

Why Choose Anranst

Bimetal Cr26+steel blow bars for APP 0606 to APK 6020: HRC 62+ wear layer with ductile steel base prevents catastrophic breakage
Application-optimized alloy selection: Mn13 for limestone, Cr26 for granite, Cr-Mo for recycling/asphalt, Bimetal for high-impact primary crushing
Full HAZEMAG impact coverage: APP 0606-1820, APK 0620-6020, APK-V series, HPI series