| Models | Wear Parts |
|---|---|
| Models | CI731-CI744, QI442 |
| Wear Parts | Blow bars, Impact plates |
| Models | jxsb79, OEM 2000 |
Manufactured from premium wear-resistant alloys including high-manganese steel, Cr-Mo alloy steel, and high-chrome cast iron.
CI731-CI744, QI442
Blow bars, Impact plates
High-speed impact element for CI-series horizontal shaft impact crushers; launches material against impact plates at 30-50 m/s
| Grade | C | Si | Mn | Cr | Mo | Ni |
|---|---|---|---|---|---|---|
| Mn13Cr2 | 1.05-1.20 | ≤1.0 | 11.5-14.0 | 1.5-2.5 | — | — |
Excellent work-hardening capability; surface hardness increases under impact, ideal for moderate to high impact crushing conditions
| Grade | C | Si | Mn | Cr | Mo | Ni |
|---|---|---|---|---|---|---|
| Cr26 | 2.0-3.3 | ≤1.0 | 0.5-1.5 | 23.0-30.0 | 1.0-3.0 | ≤1.5 |
Excellent abrasion resistance with M7C3 carbide network; 3-5x longer life than Mn steel in pure abrasive wear; ideal for vertical mill rollers and VSI rotors
| Grade | C | Si | Mn | Cr | Mo | Ni |
|---|---|---|---|---|---|---|
| Cr-Mo Alloy Steel | 0.15-0.25 | 0.30-0.60 | 0.50-0.80 | 1.00-1.50 | 0.45-0.65 | — |
Good combination of hardness and toughness; ideal for SAG mill liners, grate bars and crusher frame liners under abrasive wear
| Grade | C | Si | Mn | Cr | Mo | Ni |
|---|---|---|---|---|---|---|
| Bimetal Cr26+Carbon Steel | 2.0-3.0 / 0.15-0.25 | ≤1.0 / 0.30-0.60 | 0.5-1.5 / 0.60-1.00 | 23.0-30.0 / ≤0.50 | 1.0-3.0 / — | ≤1.0 / — |
Dual-layer casting: Cr26 wear surface + ductile steel base; combines extreme abrasion resistance with structural integrity; 1.5-2x longer life than monolithic Cr26 for large hammers
Secondary crushing surface; absorbs impact and fractures material; adjustable position controls product size
| Grade | C | Si | Mn | Cr | Mo | Ni |
|---|---|---|---|---|---|---|
| Mn18Cr2 | 1.05-1.35 | ≤1.0 | 16.0-19.0 | 1.5-2.5 | — | — |
Higher Mn content provides superior work-hardening depth; 20-30% longer service life than Mn13 in high-compression applications
Secondary impact surface in CI crusher; material is thrown against it after initial rotor impact
| Grade | C | Si | Mn | Cr |
|---|---|---|---|---|
| Mn13Cr2 | 1.05-1.35 | ≤1.0 | 11.0-14.0 | 1.5-2.5 |
Standard work-hardening steel; cost-effective for moderate impact applications
| Grade | C | Si | Mn | Cr |
|---|---|---|---|---|
| Mn18Cr2 | 1.05-1.35 | ≤1.0 | 16.0-19.0 | 1.5-2.5 |
Superior work-hardening depth; 20-30% longer life than Mn13 in high-compression applications