What wear parts are available for Metso C-Series Jaw Crushers?

Anranst supplies complete wear parts for Metso C-Series Jaw Crushers, including jaw plates, cone liners, blow bars, and other critical wear components. All parts are OEM-compatible and available in multiple material grades (Mn13Cr2, Mn18Cr2, Cr26 high-chrome iron, Cr-Mo alloy steel, WC-Co cemented carbide) to match your specific ore conditions.

What materials does Anranst recommend for Metso C-Series Jaw Crushers wear parts?

Material selection depends on your crushing application: Mn13Cr2 (ASTM A128 B-2) for moderate impact with work-hardening; Mn18Cr2 for harder abrasive feed with 30-50% longer life; Cr26 high-chrome iron for high-abrasion low-impact zones; Cr-Mo alloy steel for SAG mill liners; WC-Co for HPGR studs. Our engineers can recommend the optimal grade based on your ore characteristics.

How long is the delivery time for Metso C-Series Jaw Crushers wear parts?

Standard sizes are available for rapid delivery. Custom orders typically ship within 4-6 weeks. Emergency supply is available for critical operations with 72-hour delivery for in-stock items. Contact our sales team for specific delivery estimates.

Are Anranst wear parts compatible with OEM Metso equipment?

Yes. All Anranst wear parts are manufactured to OEM dimensions with guaranteed interchangeability. We use CMM inspection against OEM drawings and provide full metallurgical traceability. No modifications needed for drop-in replacement.

Overview

Technical Specs

Wear Parts

Metso

C-Series Jaw Crushers

Name: C-Series Jaw Crushers — Metso
Brand: Metso
Availability: InStock

Metso C-series jaw crushers are engineered for the toughest feed materials. The deep symmetrical crushing chamber with optimized nip angle maximizes feed acceptance and capacity. C-series models from C80 to C200 handle primary crushing in mining and quarrying, with throughput up to 800 tph. Anranst jaw plates in Mn13Cr2, Mn18Cr2 and premium Mn22Cr2Mo provide optimal work-hardening performance matched to your specific application.

Typical Applications

Primary crushing in miningquarryingrecyclingconstruction.

Factory

Production Gallery — Anranst Workshop

C-Series Jaw Crushers - Anranst Workshop

Technical Data

C-Series Jaw Crushers — Models

Models	Wear Parts
Models	C80-C200
Capacity	50-1,200 tph
Max Feed	Up to 1,200mm
CSS Range	40-300mm
Power	75-400 kW
Models	sher 1111

Wear Parts

Jaw Plates: High-Mn Steel (Mn13Cr2-Mn22Cr2), optional TiC composite reinforcement. Cheek Plates: Chromium white iron or Mn steel depending on application.

Wear Parts

C-Series Jaw Crushers Wear Parts

Models

C80-C200

Wear Parts

Jaw plates, Cheek plates, Toggle plates

Jaw Plate (Fixed & Swing)

Primary crushing surfaces; fixed plate anchors frame while swing plate oscillates to compress material; tooth profile determines nip angle and throughput

Mn13Cr2ASTM A128 Grade B-2 / GB ZGMn13-2

HardnessHB 210-260 (work-hardens to HRC 45-55)

ToughnessAKV ≥ 80J

Tensile Strength≥ 750 MPa

Yield Strength≥ 380 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Mn13Cr2	1.05-1.20	≤1.0	11.5-14.0	1.5-2.5	—	—

Excellent work-hardening capability; surface hardness increases under impact, ideal for moderate to high impact crushing conditions

Mn18Cr2ASTM A128 Grade B-4 / GB ZGMn18Cr2

HardnessHB 230-300 (work-hardens to HRC 48-58)

ToughnessAKV ≥ 60J

Tensile Strength≥ 800 MPa

Yield Strength≥ 420 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Mn18Cr2	1.05-1.35	≤1.0	16.0-19.0	1.5-2.5	—	—

Higher Mn content provides superior work-hardening depth; 20-30% longer service life than Mn13 in high-compression applications

Mn22Cr2MoPremium Hadfield / GB ZGMn22Cr2Mo

HardnessHB 250-320 (work-hardens to HRC 50-60)

ToughnessAKV ≥ 50J

Tensile Strength≥ 850 MPa

Yield Strength≥ 450 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Mn22Cr2Mo	1.10-1.40	≤1.0	20.0-24.0	1.5-2.5	0.30-0.60	—

Ultra-high Mn + Cr-Mo alloying; maximum work-hardening depth for extreme impact conditions; 30-50% longer life than Mn18

Cheek Plate / Side Liner

Protects crusher frame sides from abrasive wear; maintains crushing chamber width for consistent product size

Mn13Cr2ASTM A128 Grade B-2 / GB ZGMn13-2

HardnessHB 210-260 (work-hardens to HRC 45-55)

ToughnessAKV ≥ 80J

Tensile Strength≥ 750 MPa

Yield Strength≥ 380 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Mn13Cr2	1.05-1.20	≤1.0	11.5-14.0	1.5-2.5	—	—

Excellent work-hardening capability; surface hardness increases under impact, ideal for moderate to high impact crushing conditions

Toggle Plate / Toggle Seat

Transmits crushing force to swing jaw; acts as safety fuse to protect crusher from uncrushable tramp iron

Cr-Mo Alloy SteelASTM A217 WC6/WC9 / GB ZG15CrMo

HardnessHRC 42-52

ToughnessAKV ≥ 25J

Tensile Strength≥ 750 MPa

Yield Strength≥ 550 MPa

Grade	C	Si	Mn	Cr	Mo	Ni
Cr-Mo Alloy Steel	0.15-0.25	0.30-0.60	0.50-0.80	1.00-1.50	0.45-0.65	—

Good combination of hardness and toughness; ideal for SAG mill liners, grate bars and crusher frame liners under abrasive wear

Cheek Plate (Side Liner)

Protects crusher side walls from material abrasion; easily replaceable wear component

Mn13Cr2ASTM A128 Grade B-2 / GB ZGMn13Cr2

HardnessHB 210-260 (work-hardens to HRC 45-55)

ToughnessAKV ≥ 80J

Tensile Strength≥ 750 MPa

Yield Strength≥ 380 MPa

Grade	C	Si	Mn	Cr
Mn13Cr2	1.05-1.35	≤1.0	11.0-14.0	1.5-2.5

Standard work-hardening steel; cost-effective for moderate impact applications

Mn18Cr2ASTM A128 Grade B-4 / GB ZGMn18Cr2

HardnessHB 230-300 (work-hardens to HRC 48-58)

ToughnessAKV ≥ 60J

Tensile Strength≥ 800 MPa

Yield Strength≥ 420 MPa

Grade	C	Si	Mn	Cr
Mn18Cr2	1.05-1.35	≤1.0	16.0-19.0	1.5-2.5

Superior work-hardening depth; 20-30% longer life than Mn13 in high-compression applications

Toggle Plate & Seat

Safety component that breaks under overload to protect crusher frame; also sets crushing chamber CSS

ASTM A27ASTM A27/27M Grade N-2

HardnessHB 170-210

ToughnessAKV ≥ 30J

Tensile Strength≥ 485 MPa

Yield Strength≥ 250 MPa

Grade	C	Si	Mn
ASTM A27	0.25-0.35	≤0.60	≤0.70

General-purpose carbon steel casting for thrust plates and non-wear structural parts

ASTM A148ASTM A148/148M Grade 175-145

HardnessHRC 35-45

ToughnessAKV ≥ 25J

Tensile Strength≥ 1200 MPa

Yield Strength≥ 1000 MPa

Grade	C	Si	Mn	Cr	Mo
ASTM A148	0.20-0.35	≤0.60	≤1.0	≤0.50	≤0.20

High-strength structural cast steel for toggle plates and high-stress frames

Why Choose Anranst

Patented tooth profile design optimized for C80-C200 feed openings; improves nip angle by 3-5° for higher throughput
Mn22Cr2Mo option for primary crushing of high-silica ore (>60% SiO₂); 30-50% longer life than standard Mn13
Reversible jaw plate design doubles service life; precision machined contact surface prevents premature cracking
Full C-series coverage: C80, C96, C100, C105, C110, C125, C130, C140, C145, C150, C160, C200